吉田 雅幸*; 西端 樹*; 松田 朋己*; 伊藤 佑介*; 杉田 直彦*; 城 鮎美*; 菖蒲 敬久; 荒河 一渡*; 廣瀬 明夫*; 佐野 智一*
Journal of Applied Physics, 132(7), p.075101_1 - 075101_9, 2022/08
被引用回数：5 パーセンタイル：64.66(Physics, Applied)This study aims to investigate the influence of the pulse duration on the mechanical properties and dislocation density of a aluminum alloy treated using dry laser peening. The results of the micro-Vickers hardness test, residual stress measurement, and dislocation density measurement demonstrate that over a pulse duration range of 180 fs to 10 ps, the maximum peening effects are achieved with a pulse duration of 1 ps. Moreover, the most significant dry laser peening effects are obtained by choosing a pulse duration that achieves a laser intensity that simultaneously generates the strongest shock pressure, suppresses optical nonlinear effects, and realizes the least thermal effects, which weaken the shock effects.
熊谷 正芳*; 秋田 貢一; 今福 宗行*; 大谷 眞一*
Advanced Materials Research, 996, p.39 - 44, 2014/08
被引用回数：6 パーセンタイル：93.33(Engineering, Mechanical)ショットピーニング(SP)およびレーザーピーニング(LP)を施工したオーステナイトステンレス鋼の微視組織をX線ラインプロファイル解析法によって調査した。SP、LPの両試験片ともほぼ同様の残留応力深さ分布を有するが、微視組織はピーニング施工表面のみならず、表面から数ミクロン深さにおいても微視組織は異なっていた。転位密度はSP試験片のほうがLP試験片よりも高く、また、結晶子サイズはSPのほうがLPよりも小さかった。
千代 隼久*; 秋田 貢一*; 佐野 雄二*; 水田 好雄*; 玉置 悟司*; 菖蒲 敬久
no journal, ,
本研究では、極表層に残留応力を付与できる低エネルギーのレーザーピーニング4)(Low-energy laser peening: LLP)を電磁鋼板の打抜き加工面に適用し、残留応力の改善とそれによる疲労強度向上を試みた。実験は実験室系X線及び放射光X線を利用した、表面から内部に至るひずみ分布計測を行った。その結果、打抜きによって発生した高い引張残留応力がLLP施工によって圧縮残留応力に転換されること、LLP施工の圧縮残留応力生成によってバランスする引張残留応力は非常に小さいこと、そして、LLP施工時に発生する腐食を抑えたWEDM試験片において疲労強度が大幅に改善されることを明らかにした。
菖蒲 敬久; 冨永 亜希; 木曽原 直之; 前田 敏男*; 山岸 隆一郎*; 沖原 伸一朗*; 坪井 昭彦
no journal, ,
積層造形の課題である表面引張応力改善としてレーザーピーニングが有効であることからその照射前後の応力分布の変化を放射光X線で評価し、明らかに大きく改善があることを明らかにした。